Scellant Polysulfure à Deux Composants (fabriqué en Chine)

N ° de modèle: Divers Morphologie: Matériel d'émulsion d'eau: Agent principal de polysulfure Composition: Promoteur de polysulfure thixotrope Composition: Agent de durcissement Couleur: Noir Scellant Couleur: Selon vos besoins Durée de conservation: 12 Paquet de transport de Monthes: Selon vos conditions Origine: Hebei, Chine Fonction de liaison: Adhésif sous-marin Application: Construction, verre isolant Classification: Durcissement de la pièce Caractéristique: Imperméable Composition: Matière organique Marchés d'exportation: Global OEM & ODM Service: Oui Marque: jianfeng Spécification: ISO9001 / TS16949 Code SH: 522338 kent \ n téléphone mobile: + 86-15233296877 \ nTel: 86-318-5106277 \ nFax: 86-0318-5106277 \ nSite Web: www.prolianz.com \ nSociété: Hengshui Jianfeng Engineering Rubber co., LTD. \ n \ n

Product Use:  1: Glue-coating before glue coping withered material surface cleaning, clean before coating. Otherwise, it will affect the adhesive seal.  2: Takes out A and B two components according to 10: 1 proportion to carry on the mix agitation to be even, achieves the achromatism.  3: Manual or mechanical operation must arrange a direction coating and put some pressure, prevent the air wrapped into.  4: Construction of the ambient temperature maintained at above 5 ° C

Packaging into large, medium and small 1, large package: Group A[300KG] Group B [33.3KG] 2, medium package: Group A[30KG] Group B[3.35KG] 3, small package: Group A[4.5KG × 5 barrels of group B were] Group B[0.5KG × 5]

Product  features 1,  Has a good weather ability, durability, use a long time no cracks; 2,To the sealed components it has fully stable adhesion and durable adhesion, coagulation in water     soil have long-term adhesion; 3,Water vapor transmittance is extremely low, the two-component polysulfide sealant has very  good        waterproof function; 4,Against fungi, best  bacteria resistance; 5,Good construction work, the two-component polysulfide sealant can be fill into the joint very good.        6. no produce pollution for the sealing structure, no corrosion, and  the two-component polysulfide sealant has no harm to human body.

Under the conditions of the 23±2 °C and the R.H. 50±5%
Item		Component A			Component B
Viscosity(Pa's)		4000			800
Appearance		Fine, smooth and homogeneous			fine, smooth and grease-like
Color		White			Black
Density(g/em 3 )		1.75±0.1			1.52±0.1
Mixed Component A and Component B at 10:1 by weight, under the conditions of 23±2 °C and the R.H. of 50±5%
Item			Standard		Result	Test method
Resistance to flow, mm	Vertical		≤3		0.8	GB/T 1 13477
	Level		No distortion		No distortion
Application Time, 30min ,S			≤10		4.8
A:B=10:1, Under the conditions of the  23±2 °C and the R.H. of 50±5%, after 7days of curing:
Item				Standard	Result	Test method
Durometer hardness (Shore A)					45	GB/T 1 531
Tensile strength , MPa				MPa	0.8	GB/T 1 13477
Permeation rate of evaporation (g/m 2 .d)				≤15	8	GB/T 1 1037
GB/T 1 13477					25HM	JC/T 1 486

\ n

Groupes de Produits : Série d'étanchéité > Scellant polysulfure